Catalytic degradation of toxic organic dye using an aluminum-doped Cu0.4Zn0.6-xAlxFe2O4 (x = 0.0, 0.2, 0.4, 0.6) spinel ferrite in a photo-Fenton system

Catalytic activity of spinel ferrite in breaking down toxic dye materials are promising due to their uniqueness. In this study, aluminum-doped copper zinc ferrite, Cu_0.4Zn_0.6-xAl_xFe₂O₄ (x = 0.0, 0.2, 0.4, 0.6), a catalyst for toxic dye degradation is synthesized through chemical co-precipitation route. The formation of the spinel ferrite catalyst is initially confirmed by Fourier transform infrared spectra, which shows the frequency of metal-oxygen bond vibration at 539 and 427 cm⁻¹ attributed to the tetrahedral and octahedral sites respectively. Higher intensity sharp peak of X-ray diffraction for (311) plane is the evidence for the phase purity and the formation of spinel ferrite. The crystallite size is found to decrease with the increase of Al³⁺ ion. The surface structure of the obtained particles is investigated using a scanning electron microscope. Analyses of the material's magnetic characteristics using a vibrating sample magnetometer (VSM) revealed that it is, in fact, a soft magnet, as evidenced by the loop of its hysteresis, which is narrow. The catalytic degradation of methylene blue dye under the mechanism of the photo-Fenton process is studied with the obtained spinel ferrites and the result is found to be as high as 96.5%. The process follows pseudo-second order kinetics and the Langmuir isotherm.     

大肠杆菌吸附-化学还原法用废含金催化剂制备金纳米线

采用大肠杆菌吸附-化学还原法,以大肠杆菌(ECCs)为模板、十六烷基三甲基溴化铵为保护剂、抗坏血酸为还原剂,由废含金催化剂制备金纳米线(AuNWs)。采用XRD,SEM,TEM等技术对AuNWs进行表征。研究了AuNWs对罗丹明6G(R6G)和4-巯基苯甲酸(4-MBA)的拉曼散射信号的增强效果。实验结果表明:在制备过程中加入微生物ECCs,可使金回收率提高约20百分点;当溶液pH小于4时,反应2 h后,有大量呈线状的AuNWs聚集沉降,金回收率可达99%1以上。表征结果显示,AuNWs呈多晶结构,晶格间距为0.23 nm。表面增强拉曼散射分析表明,AuNWs对R6G和4-MBA具有良好的拉曼光谱增强性能。     

Feasibility of honeycomb monolith supported sugar catalyst to produce biodiesel from palm fatty acid distillate (PFAD)

Carbon coated monolith was prepared by sucrose solution 65 wt.% via dip-coating method. Sulfonation of incomplete carbonized carbon coated monolith was carried out in order to synthesize solid acid catalyst. The textural structure characteristics of the solid acid catalyst demonstrated a low surface area and pore volume. Palm fatty acid distillate (PFAD), a by-product of palm oil refineries, was utilized as oil source in biodiesel production. The esterification reaction subjected to different reaction conditions was performed by using the sulfonated carbon coated monolith as heterogeneous catalyst. The sulfonation process had been performed by using vapour of concentrated H₂SO₄ that was much easier and efficient than liquid phase sulfonation. Total acidity value of carbon coated monolith was measured for unsulfonated sample (0.5 mmol/g) and sulfonated sample (4.2 mmol/g). The effect of methanol/oil ratio, catalyst amount and reaction time were examined. The maximum methyl ester content was 89% at the optimum condition, i.e. methanol/oil molar ratio (15:1), catalyst amount (2.5 wt.% with respect to PFAD), reaction time (240 min) and temperature 80 °C. The sugar catalyst supported on the honeycomb monolith showed comparable reactivity compared with the sugar catalyst powder. However, the catalyst reusability studies showed decrease in FFA% conversion from 95.3% to 68.8% after four cycles as well as the total acidity of catalyst dropped from the value 4.2 to 3.1 mmol/g during these cycles. This might be likely due to the leaching out of SO₃H group from the sulfonated carbon coated monolith surface. The leaching of active species reached a plateau state after fourth cycle.     

Safety assessment of the film boiling chemical vapor infiltration (FB-CVI) process through a system-theoretic accident model and process (STAMP)

Film boiling chemical vapor infiltration (FB-CVI) is considered as one of the fastest process methodologies for manufacturing carbon-carbon (C–C) composite products and possesses various advantages compared to conventional methodologies. However, there are safety concerns associated with this process for large-scale manufacturing, mainly owing to the intrinsic nature of the precursor and the process conditions. Considering the multifunctional interactions of the various systems during the process, a system-theoretic process analysis (STPA)/system theoretic accident model and process (STAMP) model is used to perform a safety analysis of the hazardous states of the FB-CVI process at the system level. As a case study, the FB-CVI process equipment employed for the manufacturing of C–C composites is considered. The safety constraints present in the system are assessed for adequacy through a hazard analysis by STPA/STAMP. The analysis through STPA/STAMP demonstrated the capability to create proactive strategies for the design and realization of process equipment that can be employed to manufacture C–C composite products through the FB-CVI process.     

火灾高温下CFRP加固钢筋混凝土梁温度场分析

综合国外CFRP加固混凝土结构抗火试验相关研究,总结了CFRP的高温热工性能参数。用ANSYS软件对火灾高温下不同情况(无防火保护层和有防火保护层)和不同工况(防火涂料涂抹形式)下CFRP加固后的钢筋混凝土梁进行了温度场数值模拟研究。结果表明,防火涂料厚40 mm时,梁耐火极限可达2.5小时以上,且底面和两侧面全面涂抹防火涂料的防火效果最好。本文研究有助于进一步深入认识CFRP加固钢筋混凝土结构在高温下的力学性能和耐火极限,且对CFRP加固后的结构防火设计具有一定的指导意义。     

Study on Assessing Economic Vulnerability of Small Island Regions

The main purpose of this study is to assess economic vulnerability of small island development regions as part of their sustainability constraints. By combining economic and environmental time series data, we assessed a composite index of economic vulnerability which is constructed from three exogenous variables, namely economic exposure, economic remoteness, and economic impact of environmental and natural disasters. We used the Amami Islands, Kagoshima Prefecture, Japan as the case studies for this paper.The results indicated that using a gross island products based valuation index, Kikaijima is the most vulnerable island in the Amami Islands with a composite economic vulnerability index (CEVI) value of 0.678, while by using a per capita based index, Okinoerabujima is considered the most vulnerable island with a CEVI value of 0.680. From the results we also revealed that smaller islands have relative higher vulnerability than the bigger one, which also confirms some previous country-level vulnerability studies.However, it is matter of fact that some islands that have relatively high vulnerability also have good economic performance as shown by their per capita income. In this regard, it can be argued that the success of these small islands could have been achieved in spite of and not because of their inherent vulnerability conditions as an indicator of sustainability constraint. Regarding these findings, we also examined a comparison between vulnerability results and the preliminary concept of an island's resilience in order to capture another perspective on sustainability assessment in a small island region.     

MnO2/Al2O3催化剂-微气泡臭氧体系催化降解喹啉及其机理

制备了纳米MnO₂,并以Al₂O₃为载体制备了掺杂型MnO₂/Al₂O₃颗粒催化剂.催化剂焙烧温度和时间分别为500℃和4 h、MnO₂质量分数为8%时,催化剂具有最高的臭氧催化氧化活性.SEM分析表明,纳米MnO₂均匀分布于Al₂O₃载体表面.MnO₂/Al₂O₃催化剂的比表面积（BET）为183.22 m²·g^-1,平均孔容为0.27 cm³·g^-1,平均孔径为4.87 nm.建立了MnO₂/Al₂O₃催化剂-微气泡臭氧催化反应体系,研究了该体系对喹啉的降解去除效果及其机理.臭氧微气泡的平均粒径为61.7 μm.微气泡臭氧投量为30 mg·L^-1时,反应60 min后喹啉去除率能达到95%以上;反应20 min后,MnO₂/Al₂O₃催化剂-微气泡臭氧体系对实际煤化工废水二级出水的TOC去除率可达到55%以上.以叔丁醇作为分子探针,证明了羟基自由基（·OH）氧化作用在臭氧微气泡催化氧化体系中对喹啉的降解起到主导作用.     

MnFe2O4磁性纳米棒非均相Fenton催化降解水中四环素的研究

采用水热合成法成功制备出MnFe₂O₄磁性纳米棒（s-MnFe₂O₄）,并考察了商品化的Fe₃O₄、MnFe₂O₄和合成的s-MnFe₂O₄纳米棒这3种磁性纳米颗粒作为非均相Fenton催化剂降解水中四环素抗生素的性能.同时,采用X射线衍射（XRD）、透射电镜（TEM）、N₂吸附-脱附、振动样品磁强计（VSM）及X射线光电子能谱（XPS）等技术对催化剂的理化性质进行了表征.非均相Fenton催化降解四环素的结果表明,s-MnFe₂O₄具有最高的催化活性,反应180 min,四环素的去除率可以达到87.6%,TOC的去除率达到47.5%.自由基捕获试验证实了羟基自由基（·OH）是非均相Fenton氧化过程中的主要活性物种.s-MnFe₂O₄磁性纳米棒的高催化活性归因于其表面拥有较高含量的Mn³⁺和Fe²⁺物种,它们的存在能加速界面电子的转移效率,从而促进·OH的生成.合成的s-MnFe₂O₄催化剂具有良好的稳定性,循环使用6次,四环素的去除率仅从87.6%降低到80.2%,且氧化过程中活性组分的流失很少.     

电场与MnxCey催化剂在苯氧化反应中的协同效应及机理探究

挥发性有机物（VOCs）大量排放已成为日益严重的环境问题,为了实现VOCs的高效去除,本文采用自蔓延燃烧合成法制备了一系列锰铈复合氧化物催化剂,将稳恒直流电场引入典型VOCs气体苯的催化氧化过程,并基于不同电场条件下催化剂的理化性质表征结果进行机理分析.实验结果表明,Mn_xCe_y催化剂对含苯废气的去除有良好的效果,稳恒直流电场显著促进了催化剂的活性,其中Mn₁Ce₃的催化性能最佳,电流为5 mA时,Mn₁Ce₃催化剂在155℃可达到50%的苯转化率,在202.4℃可达到90%的苯转化率,对应的转化温度T₅₀和T₉₀比传统方法分别降低了62.4℃和48.3℃,且电场中的反应活化能由52.32 kJ·mol^-1降低至32.31 kJ·mol^-1.根据实验现象及表征结果,发现协同效应与活性位点的快速持续再生及活性氧物种的转化有关,由此提出苯在Mn_xCe_y催化剂上的氧化机理及电场协同催化的反应模型.     

Density functional theory (DFT) studies of vanadium-titanium based selective catalytic reduction (SCR) catalysts

Based on density functional theory (DFT) and basic structure models, the chemical reactions on the surface of vanadium-titanium based selective catalytic reduction (SCR) denitrification catalysts were summarized. Reasonable structural models (non-periodic and periodic structural models) are the basis of density functional calculations. A periodic structure model was more appropriate to represent the catalyst surface, and its theoretical calculation results were more comparable with the experimental results than a non-periodic model. It is generally believed that the SCR mechanism where NH₃ and NO react to produce N₂ and H₂O follows an Eley-Rideal type mechanism. NH₂NO was found to be an important intermediate in the SCR reaction, with multiple production routes. Simultaneously, the effects of H₂O, SO₂ and metal on SCR catalysts were also summarized.